PP 1100N

Mã Sản Phẩm: PP 1100N

Description

Advanced-PP 1100 N is a medium flow polypropylene homopolymer for general injection molding applications.

Melt Flow Index (MI)

12.0

Material Group

PP INJECTION (ÉP)

Producer

APC

Origin

Arabic

Application

Pressing plastic leather goods, bottle caps, lids, ropes and belts.

Applications

Application Closures,Furniture, Housewares, General injection molding.

Regulatory Information: 

The grade Advanced-PP 1100N and additives incorporated comply with United States FDA Regulation 21CFR 177.1520 Olefin Polymers and European Regulation (EU) 10/2011 (and its amendments). Specific information is available upon reques

Properties
Values
Units SI
Test methods
Polymer properties
Melt flowrate index (230°C / 2.16 KG)


Tensile modulus of elasticity (v= 1 mm/min)
Tensile stress at yield (v= 50 mm/min)Tensile Tensile strain at yield (v= 50 mm/min)
Tensile strain at break (v= 50 mm/min)
Charpy impact strength unnotched (+23°C)
Charpy impact strength notched (+23°C)
Izod Impact strength notched (+23°C)Ball indentation hardness ( H 358/30)



Melting point, DSC
Heat deflection temperature
-------------- HDT/B ( 0.45 Mpa)
Vicat softening temperature
---------------- VST/A50 (10 N)



Density
g/10 min


MPa
MPa
%
%
kJ/m2
kJ/m2
kJ/m2
MPa



°C
°C

°C



g/cm3
ISO 1133


ISO 527-2
ISO 527-2
ISO 527-2
ISO 527-2
ISO 179/1eU
ISO 179/1eA
ISO 180/1A
ISO 2039-1


ISO 3146
ISO 75-2

ISO 306



ISO 1183

12

1550

35

8

>>50

110

3.0

3

78

163

85

154

0.91

Mechanical
Thermal
Other 

Values given here are typical and should not be interpreted as specification. In a view of many factors that may affects processingand application, these data do not relieve the receiver to this information from the responsibility of carry out their own test and experiments; neither do they imply any legally binding assurance of certain properties or of suitability for specific purpose of the product made with or on the basis of the information in this publication.