LDPE 4025AS
Mã Sản Phẩm: LDPE 4025AS
Description
TASNEE LD 4025AS is a Low Density Polyethylene with a Melt Flow Rate of 4.0 g/10min (190°C/2.16kg). TASNEE LD 4025AS is mainly recommended for thin-gauge with high clarity film applications. It contains both slip agent and anti-blocking additives and has a suitable molecular structure to produce film with excellent mechanical properties. TASNEE LD 4025AS can be easily processed on all types of extruders designed for polyethylene. The melt temperature is suggested to be in the range of 150 – 190°C. Excellent properties of the film are achieved with a blow - up ratio of 2.5:1 and recommended film thickness range from 15 to 40 μm.
Melt Flow Index (MI)
4
Material Group
LLDPE FILM
Producer
TASNEE
Origin
Arabic
Application
Types of fill, foam
TYPICAL APPLICATIONS: Shrink
Film, Food Packaging Film, Blow Film and Cast Film.
PRODUCT CHARATERISTICS
Features: Anti-Blocking and Slip Additives, Good Optical Properties, Good Processability, Low Friction and Good Stiffness.
Properties
Values
Units SI
Test methods
Physical
Density
Melt Flow Rate (190°C/2.16 kg)
Melting Temperature
Vicat Softening Temperature (A50 (50 OC/h 10N))
4
923
g/cm³
g/10 min
°C
°C
ISO 1183
ISO 1133
ISO 3146
ISO 306
Mechanical
Tensile Modulus
Tensile Stress @ Yield
Tensile Strain @ Break (MD / TD) I
Tensile Strength (MD / TD)
Dart Drop Impact (50 µm)
Coefficient of Friction
260
11
300/600
22/15
100
<20
MPa
MPa
%
MPa
g
%
ISO 527-1,-2
ISO 527-1,-2
ISO 527-1,-3
ISO 527-1,-3
ASTM D 1709
ISO 8295
Optical
Haze
Gloss (20°)
(40°)
<9
>60
>105
%
GU
GU
ASTM D 1003
ASTM D 2457
1) (The above properties are measured on blown film of 70μm thickness, extruded at melt temperature of 180°C and a blow up ratio of 2:1)
Note: The typical properties are not to be construed as specifications