LDPE 1925AS

Mã Sản Phẩm: LDPE 1925AS

Description

TASNEE LD 1925AS is a Low Density Polyethylene with a Melt Flow Rate of 1.9 g/10min (190°C/2.16kg). TASNEE LD 1925AS is mainly recommended for shrink film applications. It contains slip agent and antiblocking additives and has a suitable molecular structure to produce film with excellent mechanical properties. TASNEE LD 1925AS can be easily processed on all types of extruders designed for polyethylene. The melt temperature is suggested to be in the range of 160 – 190°C. Excellent properties of the film are achieved with a blow - up ratio of 2:1 and recommended film thickness range from 25 to 60 μm.

Melt Flow Index (MI)

1.0

Material Group

LLDPE FILM

Producer

Tasnee

Origin

Arabic

Application

Films, shopping bags, and other types of packaging…

TYPICAL APPLICATIONS:

Bags & Pouches, Shrink Film, Food Packaging, Surface Protection.

PRODUCT CHARATERISTICS Features:

Anti-Blocking and Slip Additives, Good Optical Properties, Good Processability, Low Friction.

Properties
Values
Units SI
Test methods
Physical
Density
Melt Flow Rate
(190°C/2.16 kg)
Melting Temperature
Vicat Softening Temperature
(A50 (50 OC/h 10N))
0.925
1.90
111

94
g/10 min
g/cm³

ISO 1183

ISO 1133

ISO 3146

ISO 306

Mechanical
°C
 
°C
 

Tensile Modulus 

Tensile Stress @ Yield

Tensile Strain @ Break (MD / TD)

Tensile Strength (MD / TD)

Dart Drop Impact (50 µm)

Coefficient of Friction

260

11

250 / 600

26 / 18

110

20

MPa

MPa

%

MPa

g

%

ISO 527-1,-2

ISO 527-1,-2

ISO 527-1,-3

ISO 527-1,-3

ASTM D 1709

ISO 8295

Optical

Haze

Gloss (20°)

             (60°)

%
GU
GU

 

(1) (The above properties are measured on blown film of 70μm thickness, extruded at melt temperature of 180°C and a blow up ratio of 2:1)

Note: The typical properties are not to be construed as specifications.

ASTM D 1003

ASTM D 2457

<7

>50

>100

Extrusion